1943 steel cents are U.S. one-cent coins that were struck in steel due to wartime shortages of copper. The Philadelphia, Denver, and San Francisco mints each produced these 1943 Lincoln cents. The unique composition of the coin (low-grade steel coated with zinc, instead of the previously 95%-copper-based bronze composition) has led to various nicknames, such as wartime cent, steel war penny, zinc cent and steelie. The 1943 steel cent features the same Victor David Brenner design for the Lincoln cent which had been in use since 1909.
Due to wartime needs of copper for use in ammunition and other military equipment during World War II, the United States Mint researched various ways to limit dependence and meet conservation goals on copper usage. After trying out several substitutes (ranging from other metals to plastics) to replace the then-standard bronze alloy, the one-cent coin was minted in zinc-coated steel. This alloy caused the new coins to be magnetic and 13% lighter. They were struck at all three mints: Philadelphia, Denver, and San Francisco. As with the bronze cents, coins from the latter two sites have respectively "D" and "S" mintmarks below the date.
However, problems began to arise from the mintage. Freshly minted, they were often mistaken for dimes. Magnets in vending machines (which took copper cents) placed to pick up steel slugs also picked up the legitimate steel cents. Because the galvanization process did not cover the edges of the coins,[why?] sweat would quickly rust the metal. After public outcry, the Mint developed a process whereby salvaged brass shell casings were augmented with pure copper to produce an alloy close to the 1941–42 composition. This was used for 1944–46-dated cents, after which the prewar composition was resumed. Although they continued to circulate into the 1960s, the mint collected large numbers of the 1943 cents and destroyed them.
The steel cent is the only regular-issue United States coin that can be picked up with a magnet. The steel cent was also the only coin issued by the United States for circulation that does not contain any copper. (Even U.S. gold coins at various times contained from slightly over 2% copper to an eventual standard 10% copper to increase resistance to wear by making the pure gold coins slightly harder).
Far ahead of the 1955 doubled die cent in rarity, the 1943 copper cent is one of the notable rarities of the Lincoln cent series. An estimated 40 examples are believed to have been struck, with 13 confirmed to exist. The error occurred when copper planchets were left in the press hopper and press machines during the changeover from copper to steel blanks. Examples were discovered after the War, with the first two in 1947, and another in 1958. That example appeared in a 1958 Abe Kosoff sale, but was withdrawn prior to the sale; one mint condition Denver Mint specimen sold for over $1.7 million in 2010.
Many people have counterfeited the coin by either copper-plating normal 1943 cents (sometimes as novelties with no intent to defraud), or altering cents from the period, usually 1945, 1948, or 1949-dated coins.
The copper cents differ from their steel counterparts in four ways:
In 2019, NGC authenticated a worn 1943 cent composed of 86.41% tin and 8.37% antimony with other trace metals. The coin was discovered by a coin collector in the state of Oregon, who found it in his father's yard around 1969, and realized it was not attracted to a magnet while searching his coin collection for 1943 copper cents in 2019. The coin is likely an error or was intentionally struck as a pattern in late 1942 using an obverse die intended for the following year, though no documented evidence of a pattern with this composition has been found.
Hub AI
1943 steel cent AI simulator
(@1943 steel cent_simulator)
1943 steel cent
1943 steel cents are U.S. one-cent coins that were struck in steel due to wartime shortages of copper. The Philadelphia, Denver, and San Francisco mints each produced these 1943 Lincoln cents. The unique composition of the coin (low-grade steel coated with zinc, instead of the previously 95%-copper-based bronze composition) has led to various nicknames, such as wartime cent, steel war penny, zinc cent and steelie. The 1943 steel cent features the same Victor David Brenner design for the Lincoln cent which had been in use since 1909.
Due to wartime needs of copper for use in ammunition and other military equipment during World War II, the United States Mint researched various ways to limit dependence and meet conservation goals on copper usage. After trying out several substitutes (ranging from other metals to plastics) to replace the then-standard bronze alloy, the one-cent coin was minted in zinc-coated steel. This alloy caused the new coins to be magnetic and 13% lighter. They were struck at all three mints: Philadelphia, Denver, and San Francisco. As with the bronze cents, coins from the latter two sites have respectively "D" and "S" mintmarks below the date.
However, problems began to arise from the mintage. Freshly minted, they were often mistaken for dimes. Magnets in vending machines (which took copper cents) placed to pick up steel slugs also picked up the legitimate steel cents. Because the galvanization process did not cover the edges of the coins,[why?] sweat would quickly rust the metal. After public outcry, the Mint developed a process whereby salvaged brass shell casings were augmented with pure copper to produce an alloy close to the 1941–42 composition. This was used for 1944–46-dated cents, after which the prewar composition was resumed. Although they continued to circulate into the 1960s, the mint collected large numbers of the 1943 cents and destroyed them.
The steel cent is the only regular-issue United States coin that can be picked up with a magnet. The steel cent was also the only coin issued by the United States for circulation that does not contain any copper. (Even U.S. gold coins at various times contained from slightly over 2% copper to an eventual standard 10% copper to increase resistance to wear by making the pure gold coins slightly harder).
Far ahead of the 1955 doubled die cent in rarity, the 1943 copper cent is one of the notable rarities of the Lincoln cent series. An estimated 40 examples are believed to have been struck, with 13 confirmed to exist. The error occurred when copper planchets were left in the press hopper and press machines during the changeover from copper to steel blanks. Examples were discovered after the War, with the first two in 1947, and another in 1958. That example appeared in a 1958 Abe Kosoff sale, but was withdrawn prior to the sale; one mint condition Denver Mint specimen sold for over $1.7 million in 2010.
Many people have counterfeited the coin by either copper-plating normal 1943 cents (sometimes as novelties with no intent to defraud), or altering cents from the period, usually 1945, 1948, or 1949-dated coins.
The copper cents differ from their steel counterparts in four ways:
In 2019, NGC authenticated a worn 1943 cent composed of 86.41% tin and 8.37% antimony with other trace metals. The coin was discovered by a coin collector in the state of Oregon, who found it in his father's yard around 1969, and realized it was not attracted to a magnet while searching his coin collection for 1943 copper cents in 2019. The coin is likely an error or was intentionally struck as a pattern in late 1942 using an obverse die intended for the following year, though no documented evidence of a pattern with this composition has been found.