Salt-glaze or salt glaze pottery is pottery, usually stoneware, with a ceramic glaze of glossy, translucent and slightly orange-peel-like texture which was formed by throwing common salt into the kiln during the higher temperature part of the firing process. Sodium from the salt reacts with silica in the clay body to form a glassy coating of sodium silicate. The glaze may be colourless or may be coloured various shades of brown (from iron oxide), blue (from cobalt oxide), or purple (from manganese oxide).

Except for its use by a few studio potters, the process is obsolete. Before its demise, in the face of environmental clean air restrictions, it was last used in the production of salt-glazed sewer-pipes. The only commercial pottery in the UK currently licensed to produce salt glaze pottery is Errington Reay at Bardon Mill in Northumberland which was founded in 1878.

The earliest known production of salt glazed stoneware was in the Rhineland of Germany around 1400; it was effectively the only significant innovation in pottery of the European Middle Ages. Initially, the process was used on earthenware. By the 15th century, small pottery towns of the Westerwald, including Höhr-Grenzhausen, Siegburg, Köln, and Raeren in Flanders, were producing a salt-glazed stoneware, with the Bartmann jug a typical product. In the 17th century, salt glaze gained popularity in England as well as in Colonial America. Westerwald Pottery was characterized by stamped medallions and the use of a cobalt oxide based colorant for decoration. Production of salt glaze pottery in Westerwald ceased because of environmental considerations in 1983.

In the UK during the 17th century and 18th century, high quality salt-glazed stoneware was produced in Derbyshire, Nottinghamshire, London and Staffordshire. Salt glazed pottery was also popular in North America from the early 17th century until the early 19th century, indeed it was the dominant domestic pottery there during the 19th century. Whilst its manufacture in America increased from the earliest dated production, the 1720s in Yorktown, significant amounts were imported from Britain until around the mid-19th century.

During the 20th century, the technique was promoted for studio pottery use by Bernard Leach. In the 1950s, it was introduced into Japanese craft pottery through Leach's association with Shōji Hamada. Don Reitz introduced salt glazing into the curriculum at Alfred University in New York in 1959, and it subsequently spread to other American universities with ceramic art programs.^{[citation needed]}

Due to concerns of significant amount of air pollution resulting from the process environmental clean air restrictions led to the demise of widespread use of salt glazing. It was last used on any large scale for the production of salt-glazed sewer-pipes, and other than limited use by some studio potters the process is obsolete, although there are reports of it still being used for sewer-pipes in India.

Experiments in stoneware production began in England during the second part of the 17th century. The earliest evidence has been dated 1650–1700 at the site of a kiln at Woolwich Ferry, London. The similarity of the ware to German products of a similar era has led it to be attributed to immigrant potters.

A significant English manufacturer of salt glaze pottery was John Dwight at the Fulham Pottery, which he founded in 1672. In a related patent application, which was granted in 1671, he also claimed to have "discovered the mystery of transparent earthenware commonly knowne by the name of porcelaine or China and Persian ware."