Rietveld refinement
Rietveld refinement is a technique described by Hugo Rietveld for use in the characterisation of crystalline materials. The neutron and X-ray diffraction of powder samples results in a pattern characterised by reflections (peaks in intensity) at certain positions. The height, width and position of these reflections can be used to determine many aspects of the material's structure.
The Rietveld method uses a least squares approach to refine a theoretical line profile until it matches the measured profile. The introduction of this technique was a significant step forward in the diffraction analysis of powder samples as, unlike other techniques at that time, it was able to deal reliably with strongly overlapping reflections.
The method was first implemented in 1967, and reported in 1969 for the diffraction of monochromatic neutrons where the reflection-position is reported in terms of the Bragg angle, 2θ. This terminology will be used here although the technique is equally applicable to alternative scales such as x-ray energy or neutron time-of-flight. The only wavelength and technique independent scale is in reciprocal space units or momentum transfer Q, which is historically rarely used in powder diffraction but very common in all other diffraction and optics techniques. The relation is
The most common powder X-ray diffraction (XRD) refinement technique used today is based on the method proposed in the 1960s by Hugo Rietveld. The Rietveld method fits a calculated profile (including all structural and instrumental parameters) to experimental data. It employs the non-linear least squares method, and requires the reasonable initial approximation of many free parameters, including peak shape, unit cell dimensions and coordinates of all atoms in the crystal structure. Other parameters can be guessed while still being reasonably refined. In this way one can refine the crystal structure of a powder material from PXRD data. The successful outcome of the refinement is directly related to the quality of the data, the quality of the model (including initial approximations), and the experience of the user.
The Rietveld method is an incredibly powerful technique which began a remarkable era for powder XRD and materials science in general. Powder XRD is at heart a very basic experimental technique with diverse applications and experimental options. Despite being slightly limited by the one-dimensionality of PXRD data and limited resolution, powder XRD's power is astonishing. It is possible to determine the accuracy of a crystal structure model by fitting a profile to a 1D plot of observed intensity vs angle. Rietveld refinement requires a crystal structure model, and offers no way to come up with such a model on its own. However, it can be used to find structural details missing from a partial or complete ab initio structure solution, such as unit cell dimensions, phase quantities, crystallite sizes/shapes, atomic coordinates/bond lengths, micro strain in crystal lattice, texture, and vacancies.
Before exploring Rietveld refinement, it is necessary to establish a greater understanding of powder diffraction data and what information is encoded therein in order to establish a notion of how to create a model of a diffraction pattern, which is of course necessary in Rietveld refinement. A typical diffraction pattern can be described by the positions, shapes, and intensities of multiple Bragg reflections. Each of the three mentioned properties encodes some information relating to the crystal structure, the properties of the sample, and the properties of the instrumentation. Some of these contributions are shown in Table 1, below.
The structure of a powder pattern is essentially defined by instrumental parameters and two crystallographic parameters: unit cell dimensions, and atomic content and coordination. So, a powder pattern model can be constructed as follows:
It is easy to model a powder pattern given the crystal structure of a material. The opposite, determining the crystal structure from a powder pattern, is much more complicated. A brief explanation of the process follows, though it is not the focus of this article.
Hub AI
Rietveld refinement AI simulator
(@Rietveld refinement_simulator)
Rietveld refinement
Rietveld refinement is a technique described by Hugo Rietveld for use in the characterisation of crystalline materials. The neutron and X-ray diffraction of powder samples results in a pattern characterised by reflections (peaks in intensity) at certain positions. The height, width and position of these reflections can be used to determine many aspects of the material's structure.
The Rietveld method uses a least squares approach to refine a theoretical line profile until it matches the measured profile. The introduction of this technique was a significant step forward in the diffraction analysis of powder samples as, unlike other techniques at that time, it was able to deal reliably with strongly overlapping reflections.
The method was first implemented in 1967, and reported in 1969 for the diffraction of monochromatic neutrons where the reflection-position is reported in terms of the Bragg angle, 2θ. This terminology will be used here although the technique is equally applicable to alternative scales such as x-ray energy or neutron time-of-flight. The only wavelength and technique independent scale is in reciprocal space units or momentum transfer Q, which is historically rarely used in powder diffraction but very common in all other diffraction and optics techniques. The relation is
The most common powder X-ray diffraction (XRD) refinement technique used today is based on the method proposed in the 1960s by Hugo Rietveld. The Rietveld method fits a calculated profile (including all structural and instrumental parameters) to experimental data. It employs the non-linear least squares method, and requires the reasonable initial approximation of many free parameters, including peak shape, unit cell dimensions and coordinates of all atoms in the crystal structure. Other parameters can be guessed while still being reasonably refined. In this way one can refine the crystal structure of a powder material from PXRD data. The successful outcome of the refinement is directly related to the quality of the data, the quality of the model (including initial approximations), and the experience of the user.
The Rietveld method is an incredibly powerful technique which began a remarkable era for powder XRD and materials science in general. Powder XRD is at heart a very basic experimental technique with diverse applications and experimental options. Despite being slightly limited by the one-dimensionality of PXRD data and limited resolution, powder XRD's power is astonishing. It is possible to determine the accuracy of a crystal structure model by fitting a profile to a 1D plot of observed intensity vs angle. Rietveld refinement requires a crystal structure model, and offers no way to come up with such a model on its own. However, it can be used to find structural details missing from a partial or complete ab initio structure solution, such as unit cell dimensions, phase quantities, crystallite sizes/shapes, atomic coordinates/bond lengths, micro strain in crystal lattice, texture, and vacancies.
Before exploring Rietveld refinement, it is necessary to establish a greater understanding of powder diffraction data and what information is encoded therein in order to establish a notion of how to create a model of a diffraction pattern, which is of course necessary in Rietveld refinement. A typical diffraction pattern can be described by the positions, shapes, and intensities of multiple Bragg reflections. Each of the three mentioned properties encodes some information relating to the crystal structure, the properties of the sample, and the properties of the instrumentation. Some of these contributions are shown in Table 1, below.
The structure of a powder pattern is essentially defined by instrumental parameters and two crystallographic parameters: unit cell dimensions, and atomic content and coordination. So, a powder pattern model can be constructed as follows:
It is easy to model a powder pattern given the crystal structure of a material. The opposite, determining the crystal structure from a powder pattern, is much more complicated. A brief explanation of the process follows, though it is not the focus of this article.