Chrome plating
Chrome plating (less commonly chromium plating) is a technique of electroplating a thin layer of chromium onto a metal object. A chrome plated part is called chrome, or is said to have been chromed. The chromium layer can be decorative, provide corrosion resistance, facilitate cleaning, and increase surface hardness. Sometimes a less expensive substitute for chrome, such as nickel, may be used for aesthetic purposes.
Chromium compounds used in electroplating are toxic. In most countries, their disposal is tightly regulated. Some fume suppressants used to control the emission of airborne chromium from plating baths are also toxic, making disposal even more difficult.
The preparation and chrome plating of a part typically includes some or all of these steps:
There are many variations to this process, depending on the type of substrate being plated. Different substrates need different etching solutions, such as hydrochloric, hydrofluoric, and sulfuric acids. Ferric chloride is also popular for the etching of nimonic alloys. Sometimes the component enters the chrome plating vat while electrically live. Sometimes the component has a conforming anode made from lead/tin or platinized titanium. A typical hard chrome vat plates at about 0.001 inches (25 μm) per hour.
Some common industry specifications governing the chrome plating process are AMS 2460, AMS 2406, and MIL-STD-1501.
Hexavalent chromium plating, also known as hex-chrome, Cr6+, and chrome(VI) plating, uses chromium trioxide (CrO3, also known as chromic anhydride) as the main ingredient. Hexavalent chromium plating solution is used for both decorative and hard plating, as well as bright dipping of copper alloys, chromic acid anodizing, and chromate conversion coating.
A typical hexavalent chromium plating process is:
The activation bath is typically a tank of chromic acid with a reverse current run through it. This etches the work-piece surface and removes any scale. In some cases, the activation step is done in the chromium bath. The chromium bath is a mixture of chromium trioxide and sulfuric acid, the ratio of which varies greatly between 75:1 to 250:1 by weight. This results in an extremely acidic bath (pH 0). The temperature and current density in the bath affect the brightness and final coverage. For decorative coating the temperature ranges from 35 to 45 °C (100 to 110 °F), but for hard coating it ranges from 50 to 65 °C (120 to 150 °F). Temperature is also dependent on the current density, because a higher current density requires a higher temperature. Finally, the whole bath is agitated to keep the temperature steady and achieve a uniform deposition.
Chrome plating
Chrome plating (less commonly chromium plating) is a technique of electroplating a thin layer of chromium onto a metal object. A chrome plated part is called chrome, or is said to have been chromed. The chromium layer can be decorative, provide corrosion resistance, facilitate cleaning, and increase surface hardness. Sometimes a less expensive substitute for chrome, such as nickel, may be used for aesthetic purposes.
Chromium compounds used in electroplating are toxic. In most countries, their disposal is tightly regulated. Some fume suppressants used to control the emission of airborne chromium from plating baths are also toxic, making disposal even more difficult.
The preparation and chrome plating of a part typically includes some or all of these steps:
There are many variations to this process, depending on the type of substrate being plated. Different substrates need different etching solutions, such as hydrochloric, hydrofluoric, and sulfuric acids. Ferric chloride is also popular for the etching of nimonic alloys. Sometimes the component enters the chrome plating vat while electrically live. Sometimes the component has a conforming anode made from lead/tin or platinized titanium. A typical hard chrome vat plates at about 0.001 inches (25 μm) per hour.
Some common industry specifications governing the chrome plating process are AMS 2460, AMS 2406, and MIL-STD-1501.
Hexavalent chromium plating, also known as hex-chrome, Cr6+, and chrome(VI) plating, uses chromium trioxide (CrO3, also known as chromic anhydride) as the main ingredient. Hexavalent chromium plating solution is used for both decorative and hard plating, as well as bright dipping of copper alloys, chromic acid anodizing, and chromate conversion coating.
A typical hexavalent chromium plating process is:
The activation bath is typically a tank of chromic acid with a reverse current run through it. This etches the work-piece surface and removes any scale. In some cases, the activation step is done in the chromium bath. The chromium bath is a mixture of chromium trioxide and sulfuric acid, the ratio of which varies greatly between 75:1 to 250:1 by weight. This results in an extremely acidic bath (pH 0). The temperature and current density in the bath affect the brightness and final coverage. For decorative coating the temperature ranges from 35 to 45 °C (100 to 110 °F), but for hard coating it ranges from 50 to 65 °C (120 to 150 °F). Temperature is also dependent on the current density, because a higher current density requires a higher temperature. Finally, the whole bath is agitated to keep the temperature steady and achieve a uniform deposition.