Hubbry Logo
search button
Sign in
Microvoid coalescence
Microvoid coalescence
Comunity Hub
arrow-down
History
arrow-down
starMore
arrow-down
bob

Bob

Have a question related to this hub?

bob

Alice

Got something to say related to this hub?
Share it here.

#general is a chat channel to discuss anything related to the hub.
Hubbry Logo
search button
Sign in
Microvoid coalescence
Community hub for the Wikipedia article
logoWikipedian hub
Welcome to the community hub built on top of the Microvoid coalescence Wikipedia article. Here, you can discuss, collect, and organize anything related to Microvoid coalescence. The purpose of the hub is ...
Add your contribution
Microvoid coalescence
SEM image of microvoid coalescence seen on a ductile fracture surface of 6061-T6 Al

Microvoid coalescence (MVC) is a high energy microscopic fracture mechanism observed in the majority of metallic alloys and in some engineering plastics.

MVC fracture surface morphologies for a) tension, b) shear, and c) bending failures

Fracture process

[edit]

MVC proceeds in three stages: nucleation, growth, and coalescence of microvoids. The nucleation of microvoids can be caused by particle cracking or interfacial failure between precipitate particles and the matrix. Additionally, microvoids often form at grain boundaries or inclusions within the material.[1][2] Microvoids grow during plastic flow of the matrix, and microvoids coalesce when adjacent microvoids link together or the material between microvoids experiences necking. Microvoid coalescence leads to fracture.[3] Void growth rates can be predicted assuming continuum plasticity using the Rice-Tracey model:[2][4]

where is a constant typically equal to 0.283 (but dependent upon the stress triaxiality), is the yield stress, is the mean stress, is the equivalent Von Mises plastic strain, is the particle size, and produced by the stress triaxality:

Fracture surface morphologies

[edit]

MVC can result in three distinct fracture morphologies based on the type of loading at failure. Tensile loading results in equiaxed dimples, which are spherical depressions a few micrometres in diameter that coalesce normal to the loading axis. Shear stresses will result elongated dimples, which are parabolic depressions that coalesce in planes of maximum shear stress. The depressions point back to the crack origin, and shear influenced failure will produce depressions that point in opposite directions on opposing fracture surfaces. Combined tension and bending will also produce the elongated dimple morphology, but the directions of the depressions will be in the same direction on both fracture surfaces.

References

[edit]
  1. ^ Askeland, Donald R.; Wright, Wendelin J. (January 2015). The science and engineering of materials (Seventh ed.). Boston, MA. pp. 236–237. ISBN 978-1-305-07676-1. OCLC 903959750.{{cite book}}: CS1 maint: location missing publisher (link)
  2. ^ a b Soboyejo, W.O (2003). Mechanical properties of engineered materials. Marcel Dekker. pp. 393–394. ISBN 0-203-91039-7. OCLC 54091550.
  3. ^ Hertzberg, Richard W. Deformation and Fracture Mechanics of Engineering Materials, Fourth Edition. John Wiley and Sons, Inc, Hoboken, NJ: 1996.
  4. ^ Comprehensive structural integrity. Milne, I., Ritchie, R. O., Karihaloo, B. L. (1st ed.). Amsterdam: Elsevier/Pergamon. 2003. pp. 186–192. ISBN 978-0-08-049073-1. OCLC 190802556.{{cite book}}: CS1 maint: others (link)