Tripoli mineral

Rotten stone, sometimes spelled as rottenstone, also known as tripoli, is fine powdered porous rock used as a polishing abrasive for metal smithing, historically for the grinding of optical lenses and in woodworking. It is usually weathered limestone mixed with diatomaceous, amorphous, or crystalline silica. It has similar applications to pumice, but it is generally sold as a finer powder and used for a more glossy polish after an initial treatment with coarser pumice powder. Tripoli particles are rounded rather than sharp, making it a milder abrasive.

It is usually mixed with oil, sometimes water, and rubbed on the surface of varnished or lacquered wood with a felt pad or cloth. Rotten stone is sometimes used to buff stains out of wood. Some polishing waxes contain powdered rotten stone in a paste substrate. For larger polishing jobs, rotten stone mixed with a binder is applied to polishing wheels.

It has also been used to polish brass, such as that found on military uniforms, as well as steel and other metals. Plates used in daguerreotypes were polished using rotten stone, the finest abrasive available at the time.

It is also used to polish jewelry and in toothpastes. Its more common use is as a filler, as used in plastics, paint and rubber.[1]

Sources

[edit]

Rottenstone has been extensively worked in South Wales along the outcrop of the Carboniferous Limestone, particularly within the Brecon Beacons National Park. It occurs at the top of the sequence where the Upper Limestone Shales have been weathered. Innumerable workings were initiated and later abandoned during the course of the nineteenth century, leaving a characteristic terrain of humps and hollows. A notable example is that on the flanks of Cribarth exploited by industrial entrepreneur John Christie.[2]

In the United States it is mainly produced in Arkansas, Illinois, and Oklahoma.[citation needed]

See also

[edit]

References

[edit]
[edit]
Revisions and contributorsEdit on WikipediaRead on Wikipedia

Rotten stone

View on Grokipedia
from Grokipedia
Rotten stone, also spelled rottenstone and sometimes known as tripoli, is a fine-grained, porous, friable rock primarily composed of silica (SiO₂) derived from the decomposition of siliceous or chert. This natural material, typically light-colored and powdery when ground, has a high silica content of 97-99%, with minor impurities such as alumina, iron oxides, and lime. It is softer and finer than , making it ideal for achieving high-gloss finishes without excessive scratching. Historically, rotten stone has been mined from shallow pits and quarries, particularly along the outcrop of Carboniferous Limestone in South Wales, where it occurs as a sandy limestone layer at the contact with Millstone Grit. Extraction began in the late 18th century and continued into the early 20th century, with the material transported by sledges, tramroads, or canals to industrial centers like Swansea for polishing copper and other metals. Similar deposits have been worked in the United States, including Missouri, Oklahoma, and Arkansas, where it forms through the leaching of calcium carbonate from cherty limestones, leaving behind porous silica residues. In practical applications, rotten stone is used as a mixed with , , or alcohol to rub out finishes on wood, metal, jewelry, and lacquered surfaces, producing a mirror-like sheen in , metal smithing, and conservation work. It serves as an extra-fine (around 400-600 mesh) for final stages, often following coarser materials like , and is valued for its mild cutting action that smooths without deep abrasion. Beyond polishing, it has been employed as a filler in paints, a filter medium, and even in scouring products, though modern synthetic alternatives have reduced its industrial dominance.

Terminology

Etymology

The term "rotten stone" originates from the English adjective "rotten," which describes the material's soft, friable, and decomposed condition, setting it apart from more durable, solid stones. The name is a compound word formed in English from "rotten" and "stone," with the earliest documented use appearing in 1677 in Robert Plot's The Natural History of , where it refers to friable siliceous deposits. Historical records from the further illustrate its use in contexts, such as in James Sowerby's British Mineralogy (1802–1817), which describes rotten stone as a decomposed rock sourced from quarries, emphasizing its weathered and porous texture. In , the term is often rendered as one word, "rottenstone," reflecting its longstanding association with regions like , where miners identified it by its "rotted" appearance due to extensive . This descriptive nomenclature underscores the rock's eroded, disintegrated quality compared to intact limestone formations, a distinction noted in early geological and mining literature from the 17th and 18th centuries.

Synonyms

Rotten stone is primarily synonymous with tripoli, a term derived from the North African city of Tripoli (in modern-day Libya), where similar siliceous deposits were first exported in the 17th century as a fine abrasive; this name became a generic marketing label for imported polishing materials of this type. The one-word variant rottenstone is prevalent in American English usage, reflecting a simplified spelling in industrial and trade contexts. In French, rotten stone is commonly called tripoli for polishing applications. Welsh rotten stone, sourced from Welsh quarries and prepared for fine polishing of silver and metals in the 19th century. During the 19th century, historical polishing manuals referred to it as siliceous earth, highlighting its decomposed siliceous composition. The descriptor "rotten" in the primary name alludes to the material's friable, softened texture from natural decomposition.

Geology and Composition

Formation

Rotten stone primarily forms through the chemical weathering of siliceous limestones or cherts, in which calcium carbonate (CaCO₃) is selectively dissolved by acidic groundwater, typically carbonic acid derived from rainwater and soil respiration, leaving behind a porous, friable residue enriched in microcrystalline silica (SiO₂). This process concentrates the insoluble siliceous components, such as chert nodules or flint, into a lightweight, earthy material while the surrounding carbonate matrix is leached away over extended periods. The resulting soft, decomposed texture gives the material its descriptive name "rotten stone." In the United Kingdom, significant deposits occur at the geological contacts between the Carboniferous Limestone and the overlying Millstone Grit formations, where acidic percolation enhances dissolution in these transitional zones. Notable examples include the "Rottenstone band" within the Carboniferous Limestone sequence in the Matlock area of Derbyshire, England, where detached masses of the material form in cavities up to 20 feet deep. Similar formations are found in South Wales on Mynydd Du, also at the Carboniferous Limestone-Millstone Grit interface, representing localized weathering of sandy limestone units. Comparable deposits exist in the United States within Paleozoic-era rocks, particularly Mississippian-age limestones. In and , rotten stone, often termed tripoli, derives from the weathering of chert-bearing layers in the Boone Formation, near the Missouri-Oklahoma border, such as the quarries around Seneca. These formations originated during the period, approximately 360 to 300 million years ago, when siliceous limestones were deposited in shallow marine environments, with subsequent exposure and occurring through millions of years of tectonic uplift and without any human influence.

Mineralogical Composition

Rotten stone, also known as tripoli, is primarily composed of amorphous to microcrystalline silica (SiO₂), accounting for 80-99% of its weight depending on the deposit, with commercial grades often exceeding 98% SiO₂. Trace minerals typically include iron oxides (Fe₂O₃, 0.03-2.4%), alumina (Al₂O₃, 0.1-3.9%), and minor impurities such as titanium dioxide (TiO₂, ~0.015%); calcium oxide content remains low at less than 1% (CaO, 0.01-0.7%) due to extensive leaching of carbonates during the silica-concentrating weathering process. Compositional variations arise from source-specific geological origins; for instance, material from Derbyshire, England, tends toward higher silica purity, often approaching 90-95% SiO₂ with minimal inclusions, while Welsh rotten stone from sandy limestone units incorporates more quartz grains and detrital sand, resulting in slightly lower overall silica content and increased textural heterogeneity. When processed into powder for abrasive applications, particle sizes generally range from 0.5 to 10 microns, enabling fine polishing without surface damage. The mineralogical structure is determined through techniques like X-ray diffraction (XRD), which identifies and occasional opal-CT phases alongside a dominant amorphous silica matrix; the lack of prominent crystalline peaks underscores its disordered, porous framework, which provides the material's characteristic mild abrasiveness and non-scratching polish on delicate surfaces.

Physical Properties

Texture and Structure

Rotten stone occurs naturally as friable, porous nodules or layers of decomposed siliceous , typically exhibiting a light gray to yellowish color and a soapy or earthy tactile feel due to its soft, crumbly consistency. This material is highly porous, with the voids primarily resulting from the dissolution of during , leaving behind a siliceous that imparts a light, cotton-like quality to the rock. The contributes to its even-textured, fine granular , which lacks distinct or fossils and is often divided by irregular joints. In its powdered form, rotten stone presents an ultra-fine, flour-like consistency that feels non-gritty when dry, readily forming a smooth slurry when mixed with water or oil. The particles, derived from grinding the natural rock, have a Mohs hardness of 6.5 to 7, rendering them harder than talc but composed of the same microcrystalline silica that dominates the material's composition. The density of the powdered form ranges from 2.2 to 2.5 g/cm³, reflecting the lightweight nature of the siliceous aggregates. Microscopic examination via scanning electron microscopy (SEM) reveals irregular, sponge-like aggregates of euhedral crystals, typically 0.5 to 6 micrometers in length, which form the porous microstructure responsible for the material's absorbency and texture. These features underscore the material's origin as a highly altered silica residue, with no sharp edges or crystalline facets visible at the particle level.

Abrasiveness Characteristics

Rotten stone's abrasiveness stems from its exceptionally fine , typically 12-14 microns in diameter, equivalent to a grit level of approximately 1000-1200, which is finer than standard grades (16-18 microns for FFFF pumice). This fineness permits the achievement of mirror-like finishes on various surfaces while avoiding deep scratches, with the cutting mechanism relying on micro-abrasion from its constituent silica particles. Key performance factors include the material's moderate friability, which allows particles to break down progressively and prevents clumping during application, alongside a high of approximately 2-5 m²/g that promotes efficient absorption of lubricants such as oils or . Its near-neutral range of 6-8 ensures compatibility and safety with most substrates, minimizing risks of or surface degradation. The porous texture of rotten stone further supports slurry formation, optimizing its efficacy in operations.

Production

Sourcing and Extraction

Rotten stone deposits are primarily located in sedimentary basins, forming at contacts between and overlying grit or layers through natural processes. Sourcing occurs mainly via open-pit quarrying in shallow deposits typically 5 to 20 meters deep. Active extraction today occurs in operations in multiple states, including Missouri's Newton County (thin overburden of roughly 2 meters covers tripoli beds 0.6 to 4.3 meters thick), Arkansas's Garland County, Illinois's Alexander County, and Oklahoma's Ottawa County. Extraction techniques emphasize the material's softness, employing manual picking of surface nodules or mechanical scraping of layers using front-end loaders and trucks, with little to no blasting required. In , , , and sites, hand sorting follows initial removal to select material by texture and color. Environmental practices during extraction include dust suppression via water sprays at loading points and comprehensive site reclamation, involving replacement, regrading, and revegetation to prevent and restore . Globally, deposits are confined to such settings, with annual production around 88,700 metric tons of crude material as of the mid-1990s, dominated by U.S. suppliers following the closure of major U.K. sites. More recent U.S. data indicate processed tripoli production of 106,000 metric tons in 2019, with the vast majority used as fillers (96%) and abrasives (4%).

Milling and Preparation

The friable nature of rotten stone eases its milling, as the soft, porous silica structure requires less energy for size reduction compared to harder minerals. Raw material is first subjected to primary crushing in jaw crushers to break down large fragments into smaller pieces suitable for further processing. This is followed by secondary grinding in ball mills or attrition mills, which reduce the particles to sizes below 10 microns, producing a fine powder ideal for applications. Air classification is applied post-milling to separate and eliminate coarse fractions, yielding a consistent particle distribution with minimal oversize material. The powder then undergoes drying at 100–150°C in rotary or fluid-bed dryers to lower moisture content to under 1%, preventing clumping and ensuring stability during storage and use. Optional at higher temperatures may follow to remove residual organics and improve purity, particularly for high-grade products. Final preparation includes packaging the powder in bags from 1 to 50 pounds, with some variants pre-mixed with oils or binders for direct application in polishing compounds. Quality control relies on to confirm uniformity and , while modern automated mills , such as those employing vibrating fluid-bed dryers, routinely produce silica powders with 99% purity.

Historical Development

Early Uses

Rotten stone, a soft, porous primarily sourced from quarries in , saw its earliest documented uses as a fine in the for metal and stone polishing. Extracted from decomposed deposits near , it was described in James Sowerby's British Mineralogy (1807) as essential for lapidaries, who applied it with on lead or wheels to polish harder gemstones and metals in manufactories. This material, also known synonymously as tripoli—a term originating from imports of similar substances from Tripoli in —provided a gentle yet effective finishing agent superior to coarser abrasives. By the mid-18th century, rotten stone became integral to the cutlery trade, where it was mixed with oil and applied to wheels or benches to achieve a smooth, high-luster finish on blades and other steel implements following initial grinding stages. As detailed in contemporary accounts, such as The Penny Magazine (1843), cutlers and specialized female buffing workers relied on this powder to remove fine scratches and enhance the sheen of , contributing to Sheffield's reputation for quality exports. Similarly, in , rotten stone was powdered and used extensively in the 18th- and 19th-century tinplate and industries for buffing metal sheets, with extraction occurring via shallow opencast pits in areas like Mynydd Du. In the cultural realm of 19th-century furniture making, rotten stone played a key role in achieving high-gloss wood surfaces through French polishing techniques, where it followed coarser applications and was rubbed with oil or water for final clarification. Historical guides on , such as those outlining period finishing methods, recommended it for its ability to produce a mirror-like sheen on varnished pieces without scratching the underlying . This artisanal application underscored rotten stone's versatility in pre-industrial crafts, bridging and traditions before mechanized production expanded its scope.

Industrialization

In the early , the production of rotten stone, also known as tripoli, underwent a significant boom in the United States, driven by the development of major deposits in and . These regions, particularly around Seneca on the Missouri-Oklahoma border, saw increased mining and milling operations to supply the burgeoning , where rotten stone served as a key for vehicle bodies and components. The American Tripoli Company, a pioneer in the field, completed construction of its first dedicated mill in Seneca in December 1906, enabling large-scale processing and distribution of the material for industrial applications. World War II further accelerated demand for rotten stone due to its role in precision metal finishing for munitions, , and machinery production. U.S. production reached approximately 15,000 short tons by 1943, with output continuing at similar levels through the mid-1940s to meet military specifications. Following the war, the market for rotten stone faced challenges from the rise of synthetic s such as and aluminum oxide, which offered greater uniformity and efficiency in large-scale operations. The proportion of tripoli used as an declined from nearly 70% of output in 1970 to about 20% by the late 1990s, as demand shifted toward fillers in paints and rubber. Despite this shift, niche applications in fine polishing and fillers sustained demand, particularly in specialty manufacturing. In the , the National Institute for Occupational Safety and Health (NIOSH) recommended a reduced exposure limit of 50 µg/m³ for respirable crystalline silica in 1988, influencing OSHA practices and prompting improvements in milling processes, such as enhanced ventilation and wet processing to minimize health risks for workers; OSHA's major PEL update to 50 µg/m³ followed in 2016. The legacy of industrialization also included a decline in traditional production centers, with quarries—once key suppliers for polishing in and —largely closing by the 1950s due to competition from cheaper imports, primarily from the . As of 2023, U.S. production of tripoli was estimated at approximately 85,000 metric tons, with global output emphasizing sustainable sourcing practices, such as selective and , to mitigate environmental impacts; the (MSHA) further strengthened protections with a 2024 rule setting a PEL of 50 µg/m³ for mining operations.

Applications

Polishing and Finishing

Rotten stone is commonly employed in the final stages of to achieve a high-gloss surface after initial abrasion with coarser materials like . The process involves creating a wet by mixing the powder with , paraffin oil, or water, often enhanced with for added lubrication and sheen. This is applied to the varnished or shellacked surface using a felt pad or soft cloth, rubbed in circular motions with light pressure to level imperfections and enhance reflectivity, resulting in a smooth, mirror-like finish suitable for furniture and . For metal polishing, rotten stone is typically used as a dry powder or mixed with to buff surfaces such as silver and , removing fine scratches and oxidation without aggressive cutting. In gilding restoration, it is blended with linseed or into a fine paste and applied with a soft cloth to polish , revealing underlying bole and achieving a lustrous . The technique emphasizes gentle rubbing to avoid scratching, followed by wiping with a clean cloth to prevent residue buildup. In stone and lapidary work, rotten stone serves as a pre-polish or final abrasive for marble and gemstones, particularly softer materials, where it is mixed with oil or water to form a paste applied via buffing wheels or pads. For marble, the oil-mixed compound is rubbed onto the surface to eliminate micro-scratches and impart a satin to high-gloss sheen, while in gem polishing, a glycerin oil slurry on a damp felt wheel provides the last buffing step after pumice, yielding a clear, reflective polish on softer stones. This finer grit than pumice ensures precise control in the concluding phases. Best practices for rotten stone application include always following with thorough wiping to remove excess . It is particularly valued in the restoration of antiques, such as furniture and gilded , and musical instruments like violins, where the powder's mild action preserves delicate finishes without altering historical patinas. Safety precautions involve working in well-ventilated areas, using NIOSH-approved respirators to avoid inhalation of respirable crystalline silica dust, which can cause serious health risks including , , (COPD), and .

Industrial and Artistic Uses

Rotten stone, also known as tripoli, serves as a versatile filler in various industrial applications due to its high silica content, which provides chemical inertness and fine . In paints and coatings, it constitutes a significant portion of filler use, enhancing tint retention, , leveling, and flowability while acting as a thixotropic agent to prevent settling and improve application properties; approximately 96% of processed tripoli is employed as a filler or extender in such products, including paints, alongside plastics and rubber where it improves properties, chemical resistance, and weatherability. In rubber formulations, rotten stone functions as an extender, comprising about 5% of total annual tripoli filler production, contributing to enhanced mechanical stability without compromising flexibility. It is also incorporated into scouring powders and industrial soaps as a mild for cleaning metal and jewelry, and in ceramics for grindstones and tube-mill liners to impart texture and . Historically, rotten stone has been used as a mild in formulations to provide gentle polishing action. In niche industrial contexts, rotten stone appears in facings and as a deburring medium for and castings, leveraging its porous structure to facilitate smooth surface preparation in processes. In industrial settings, exposure to respirable crystalline silica from rotten stone is regulated by OSHA under 29 CFR .1053, with a (PEL) of 50 micrograms per cubic meter as an 8-hour time-weighted average; , exposure monitoring, and are required to mitigate risks. Annual consumption in non-polish sectors, primarily fillers and extenders, reached approximately 101,760 metric tons in , reflecting its widespread adoption in . Artistically, rotten stone is employed in gilding techniques to distress surfaces, creating an aged or matte appearance by lightly abrading the gilded layer with the powder mixed in oil or alcohol. It is also mixed into for canvas priming, adding tooth to the ground layer to improve paint adhesion and surface texture for oil or acrylic applications.

Modern Availability and Alternatives

Commercial Sources

In the United States, major suppliers of rotten stone include , offering 1-pound packs of fine for $17.99, suitable for wood surfaces. Mohawk Finishing Products provides 1-pound containers at $16.91 and 5-pound packages for $28, emphasizing its use as an extra-fine abrasive for high-gloss finishes on and . For bulk needs, mineral distributors like CB Minerals supply larger quantities to industrial users. In the , heritage brands such as Cornelissen offer 1-kilogram (approximately 2.2-pound) packs of grey rotten stone powder for £18, often sourced from imported tripoli deposits. Other suppliers like Gold Leaf Supplies provide smaller quantities starting at £8.17 excluding VAT, catering to restorers and gilders. Rotten stone is primarily available as pure powder, though it can be mixed on-site with oils or water to form pastes for application; pre-mixed versions are less common. Online retailers, including specialty sites like WoodFinishing Enterprises (with prices ranging from $6 for small jars to $173 for bulk) and platforms such as Amazon, dominate consumer sales, while industrial bulk purchases occur through mineral distributors. Market trends in the show stable retail pricing at $10–18 per pound for small packs, with wholesale options for larger volumes available at lower rates through specialized suppliers. Products often carry certifications indicating low respirable crystalline silica content, typically less than 1% as per data sheets, to minimize health risks during use.

Substitutes and Comparisons

, a fine natural derived from decomposed siliceous , has several common substitutes in applications, each suited to specific tasks based on particle size, hardness, and removal rate. , a coarser powder, serves as a cheaper alternative for initial stages, offering effective removal at a lower cost but resulting in a less refined finish compared to rotten stone's glossy outcome. Whiting, or powdered , provides a milder action ideal for gentle cleaning and filling on soft surfaces like wood or , though it lacks the cutting power of rotten stone for achieving high luster. Synthetic alumina, such as aluminum oxide powders, acts as a faster-cutting substitute for general metal and stone , but its harder particles increase the risk of micro-scratches on delicate substrates if not carefully graded. Rotten stone excels in delivering a superior fine finish on delicate surfaces like fine woods, metals, and gilded elements, where its friable nature and around 400-600 allow for progressive refinement without deep abrasion. As a natural material, it is eco-friendly and biodegradable, reducing environmental impact relative to synthetic alternatives, though users must employ masks to mitigate risks from its silica dust. Alternatives are preferable in scenarios demanding higher aggression or speed. For heavy material removal on metals or stones, emery—a corundum-based —outperforms rotten stone by cutting faster without frequent reapplication. In modern automotive buffing for glass or paint correction, cerium oxide provides quicker results on hard surfaces like windshields, though at a higher cost of $25–30 per pound versus rotten stone's approximately $14 per pound.

References

  1. https://www.geology.arkansas.gov/minerals/industrial/Tripoli.html
  2. https://pubs.usgs.gov/bul/0340j/report.pdf
  3. https://encyclopediaofarkansas.net/entries/tripoli-mining-5957/
  4. https://www.rockler.com/rotten-stone-1-pound
  5. https://www.fforestfawrgeopark.org.uk/understanding/archaeology-and-industrial-heritage/legacies-of-the-industrial-age/rotten-stone/
  6. https://canalrivertrust.org.uk/news-and-views/blogs/waterfront/canalopolis-celebrating-the-225th-anniversary-of-the-swansea-canal
  7. http://ogs.ou.edu/docs/hopper/HopperV11N6.pdf
  8. https://woodfinishingenterprises.com/shop/abrasives/rottenstone/
  9. https://cameo.mfa.org/wiki/Rottenstone
  10. https://www.merriam-webster.com/dictionary/rottenstone
  11. https://www.oed.com/dictionary/rottenstone_n
  12. https://www.c82.net/mineralogy/b240
  13. https://www.dictionary.com/browse/rottenstone
  14. https://www.wordreference.com/definition/Tripoli
  15. https://pubs.usgs.gov/myb/vol1/2019/myb1-2019-silica.pdf
  16. https://www.e-rara.ch/download/pdf/6762985.pdf
  17. https://journals.pan.pl/Content/81924?format_id=1
  18. https://geo.libretexts.org/Courses/Chabot_College/Introduction_to_Physical_Geology_%28Shulman%29/10%253A_Weathering_Sediment_and_Soil/10.03%253A_Chemical_Weathering
  19. https://depositsmag.com/2023/04/08/the-british-carboniferous-limestone/
  20. https://d9-wret.s3.us-west-2.amazonaws.com/assets/palladium/production/mineral-pubs/silica/silicmyb02.pdf
  21. https://www.kremer-pigmente.com/media/pdf/599920e.pdf
  22. http://ogs.ou.edu/docs/bulletins/B28.pdf
  23. https://www.wsgs.wyo.gov/products/wsgs-1989-ofr-04.pdf
  24. http://library.isgs.illinois.edu/Pubs/pdfs/Manuscripts/External/MS_Nelson_WJ_18.pdf
  25. https://pumicestore.com/pumice-products/pumice-finishing-grit.html
  26. https://core.ac.uk/download/pdf/17354981.pdf
  27. https://www.empireblended.com/engineered/specialtysundry-rottenstone.html
  28. https://pubs.usgs.gov/bul/0585/report.pdf
  29. https://www.epa.gov/sites/default/files/2015-10/documents/mineral-mining_dd-vol-3_1975.pdf
  30. https://d9-wret.s3.us-west-2.amazonaws.com/assets/palladium/production/mineral-pubs/silica/041494.pdf
  31. https://www.epa.gov/sites/default/files/2015-10/documents/mineral_mining_dd_1976.pdf
  32. https://www.9silica.com/PRODUCTS/Silica_sand_powder_making_mach/65.html
  33. https://www.whitemountainhistory.org/livermore-tripoli-company
  34. https://irp-cdn.multiscreensite.com/65c18930/files/uploaded/Powder-Bulk-Engineering-7-2002.pdf
  35. https://www.collinsdictionary.com/us/dictionary/english/tripoli
  36. https://etheses.whiterose.ac.uk/id/eprint/24956/2/265153_Vol2.pdf
  37. https://www.scribd.com/document/549729097/FRENCH-POLISH-IN-THE-19th-CENTURY
  38. https://americantripoli.com/wp-content/uploads/History-of-SENECA-STANDARD-tripoli-report.pdf
  39. https://search.library.wisc.edu/digital/A4VD7V2YJO3CQT8H/pages/A4UPTS5UAGXJIX8C?as=text&view=scroll
  40. https://share.mo.gov/nr/mgs/MGSData/Books/Information%20Circular/The%20Mineral%20Industry%20of%20Missouri%20in%201946%20and%201947%20with%20Total%20Production%20Summarized/IC-004.pdf
  41. https://d9-wret.s3.us-west-2.amazonaws.com/assets/palladium/production/mineral-pubs/silica/780498.pdf
  42. https://pubs.usgs.gov/myb/vol1/2018/myb1-2018-silica.pdf
  43. https://www.cdc.gov/niosh/pel88/1317-95.html
  44. https://www.federalregister.gov/documents/2016/03/25/2016-04800/occupational-exposure-to-respirable-crystalline-silica
  45. https://pubs.usgs.gov/periodicals/mcs2024/mcs2024.pdf
  46. https://www.msha.gov/regulations/rulemaking/silica
  47. https://www.woodmagazine.com/sanding-sharpening/rub-a-polyurethane-finish-the-right-way
  48. https://www.woodsmith.com/article/rubbing-out-a-high-gloss-finish/
  49. https://www.goldleafsupplies.co.uk/gilding-restoration/rottenstone/
  50. https://www.shopthegemgarden.com/rottenstone-fine-abrasive-powder-l1018164p
  51. https://www.woodfinishingenterprises.com/shop/abrasives/rottenstone/
  52. https://www.osha.gov/silica-crystalline
  53. https://www.cdc.gov/niosh/docs/2002-129/default.html
  54. https://www.osha.gov/laws-regs/regulations/standardnumber/1910/1910.1053
  55. https://easyleafproducts.nnigroup.com/product/rottenstone/
  56. https://www.naturalpigments.com/rottenstone-5-oz.html
  57. https://www.mohawkproducts.com/rottenstone-1-lb.htm
  58. https://www.mohawkproducts.com/MOHAWK-ROTTENSTONE-5-LB-PKG-p/m720-1500.htm
  59. https://cbminerals.com/rottenstone/
  60. https://www.kremer-pigmente.com/elements/resources/products/files/599920_SDS.pdf
  61. https://www.shotgunworld.com/threads/whiting-quick-substitute-for-rottenstone.52977/
  62. https://www.thoughtco.com/what-are-abrasive-minerals-1439101
  63. https://sawmillcreek.org/threads/rottenstone-and-pumice-where-in-the-scale.32287/
  64. https://rocktumbler.com/polish/
  65. https://shop.jescoproducts.com/top-quality-polish-for-tumbling/cerium-oxide-1-lb.-free-shipping/
Add your contribution
Related Hubs
User Avatar
No comments yet.